Ultramid? 8202 HS | PA6 | BASF

 二维码 3
Ultramid? 8202 HS | PA6 | BASF
材料文字说明
Ultramid? 8202 HS is a heat stabilized, low viscosity, general purpose Polyamid 6 injection molding.
It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas.

Ultramid? 8202 HS is generally recommended for drapery hardware, gears, fittings, furniture casters, bearings, handles, clips, fasteners and thin parts.
机械性能干 / 已调节单位测试标准
拉伸模量2700 / 970MPaISO 527-1/-2
屈服应力78 / 36MPaISO 527-1/-2
屈服伸长率4 / 16%ISO 527-1/-2
断裂标称应变25 / >50%ISO 527-1/-2
无缺口简支梁冲击强度, +23°CN / -kJ/m2ISO 179/1eU
无缺口简支梁冲击强度, -30°C51 / -kJ/m2ISO 179/1eU
简支梁缺口冲击强度, +23°C3.5 / -kJ/m2ISO 179/1eA
热性能干 / 已调节单位测试标准
熔融温度, 10°C/min220 / *°CISO 11357-1/-3
热变形温度, 1.80 MPa60 / *°CISO 75-1/-2
厚度为h时的燃烧性V-2 / *classIEC 60695-11-10
测试用试样的厚度0.7 / *mmIEC 60695-11-10
Yellow Card 现存Yes / *--
电性能干 / 已调节单位测试标准
体积电阻率>1E13 / -Ohm*mIEC 62631-3-1
相对漏电起痕指数- / 600-IEC 60112
其它性能干 / 已调节单位测试标准
吸水性9.5 / *%类似ISO 62
吸湿性2.7 / *%类似ISO 62
密度1130 / *kg/m3ISO 1183
流变计算用参数.价值单位测试标准
熔体密度932kg/m3-
熔体0.264W/(m K)-
熔体的比热3730J/(kg K)-
试样制备条件价值单位测试标准
注塑, 熔体温度260°CISO 294
注塑, 模具温度80°CISO 294
函数
www.campusplastics.com1E11E21E31E41E11E21E3粘度-剪切速度Ultramid? 8202 HS剪切速度 in 1/s粘度 in Pa s250°C260°C270°C
www.campusplastics.com1E11E21E31E41E31E41E51E6剪切应力-剪切速度Ultramid? 8202 HS剪切速度 in 1/s剪切应力 in Pa250°C260°C270°C
www.campusplastics.com-100-500501001502002501E11E21E31E4动态剪切模量-温度Ultramid? 8202 HS (干)温度 in °C剪切模量 in MPa
www.campusplastics.com0123456020406080100应力-应变.Ultramid? 8202 HS (干)应变 in %应力 in MPa23°C80°C120°C150°CY变形Y
www.campusplastics.com01234560500100015002000250030003500正割模量-应变.Ultramid? 8202 HS (干)应变 in %正割模量 in MPa23°C80°C120°C150°CY变形Y
典型数据
加工方法
注塑
供货形式
粒料
特殊性能
经热稳处理的/耐热的
会员登录
登录
我的资料
我的收藏
留言
回到顶部
http://www.kungyat.com http://www.wxzjhj.com http://www.honeymoon4less.com http://www.xboxdiscovery.com http://www.huilaiyun.com http://www.egiwall.com http://www.printingauckland.com http://www.audi-strasbourg.com http://www.cnshenkai.com http://www.crtx56.com http://www.magazinemedico.com http://www.ocalamarionchristmasparade.com http://www.graviola-soursop-cancercure.com http://www.kexingsuliao.com http://www.tvpornostreaming.com http://www.mm1238.com http://www.loewenstomexico.com http://www.shoujitaocan.com http://www.sdhygssm.com http://www.comoemagrecer-rapido.com http://www.gdhsph.com http://www.rallylube.com http://www.isd03.com http://www.lyxyklc.com http://www.leasidepainttoronto.com http://www.keilarsbakery.com http://www.jiasensh.com http://www.jjjj1069.com http://www.foresvision.com http://www.kyoto-sushi.com