Ultramid? 1503-2 NF2004 | PA66-GF33 | BASF

 二维码 2
Ultramid? 1503-2 NF2004 | PA66-GF33 | BASF
材料文字说明
Ultramid? 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6.
机械性能干 / 已调节单位测试标准
拉伸模量10800 / 7400MPaISO 527-1/-2
断裂应力210 / 145MPaISO 527-1/-2
断裂伸长率3 / 5%ISO 527-1/-2
无缺口简支梁冲击强度, +23°C90 / 100kJ/m2ISO 179/1eU
无缺口简支梁冲击强度, -30°C75 / 75kJ/m2ISO 179/1eU
简支梁缺口冲击强度, +23°C12 / 15kJ/m2ISO 179/1eA
简支梁缺口冲击强度, -30°C11 / 11kJ/m2ISO 179/1eA
热性能干 / 已调节单位测试标准
熔融温度, 10°C/min257 / *°CISO 11357-1/-3
热变形温度, 1.80 MPa255 / *°CISO 75-1/-2
热变形温度, 0.45 MPa264 / *°CISO 75-1/-2
其它性能干 / 已调节单位测试标准
吸水性5.7 / *%类似ISO 62
吸湿性1.7 / *%类似ISO 62
密度1400 / -kg/m3ISO 1183
函数
www.campusplastics.com02468050100150200250应力-应变.Ultramid? 1503-2 NF2004 (干)应变 in %应力 in MPa23°C40°C80°C120°C150°CB折断BBBBB
www.campusplastics.com01234567050100150应力-应变.Ultramid? 1503-2 NF2004 (湿)应变 in %应力 in MPa23°C40°C80°C120°C150°CB折断BBBBB
www.campusplastics.com02468020004000600080001000012000正割模量-应变.Ultramid? 1503-2 NF2004 (干)应变 in %正割模量 in MPa23°C40°C80°C120°C150°CB折断BBBBB
www.campusplastics.com0123456710002000300040005000600070008000正割模量-应变.Ultramid? 1503-2 NF2004 (湿)应变 in %正割模量 in MPa23°C40°C80°C120°C150°CB折断BBBBB
典型数据
加工方法
注塑


会员登录
登录
我的资料
我的收藏
留言
回到顶部
http://www.gdbj.net http://www.yang-pai.com http://www.sandiegopaintedsigns.com http://www.xskjdn.com http://www.newhealthcareenterprises.com http://www.13931560111.com http://www.homelivingroomfurniture.com http://www.drawlayer.com http://www.favoritegreekrecipes.com http://www.jiayifangjz.com http://www.profesionalesendirecto.com http://www.diligentliftservice.com http://www.southernatmospherestudios.com http://www.antoniomartinezcortado.com http://www.rosewindvalley.com http://www.usscairo.com http://www.boston-environmental.com http://www.mikequeenphotography.com http://www.goldstarrubber.com http://www.flyingspring.com http://www.rosewindvalley.com http://www.smartscoz.com http://www.oophome.com http://www.fstongsheng.com http://www.q92.net http://www.zjlg.net http://www.gzlongke.com http://www.thhjtyy.com http://www.carbonconversiontechnology.com http://www.hbyangyang.com